Fire Proof White Powder Intumescent Flame Retardant Coating Treated By Melamine
Contact me for free samples and coupons.
Whatsapp:0086 18588475571
Wechat: 0086 18588475571
Skype: sales10@aixton.com
If you have any concern, we provide 24-hour online help.
xProduct Details
| Production Name | Fire Proof White Powder Intumescent Flame Retardant Coating Treated By Melamine | Type | Chemcials Powder |
|---|---|---|---|
| Eco-friendly | Halogen-free | State | White Powder |
| Key Words | Flame Retardant | Function | Fire Prevention |
| Nitrogen | ≥17% | Phosphorus | ≥28% |
| High Light | Melamine Coating Treated Intumescent Flame Retardant,Fireproof Intumescent Flame Retardant |
||
Product Description
Fire Proof White Powder Intumescent Flame Retardant Coating Treated By Melamine
APP(ammonium polyphosphate) is mainly polymerized from monomeric diphosphorus pentaoxide(P2O5) and diammonium hydrogenorthophosphate(DAP)
APP is flame retardant using expansion mechanism.
APP decomposes ammonia gas and polyphosphoric acid at 275 ℃. Ammonia dilutes the oxygen concentration and at the same time expands and loosens the carbon layer to isolate heat.
APP is halogen free, environmental friendly.
Product description:
Melamine modified APP-II is a flame retardant based on phosphorus /nitrogen synergism, free formaldehyde, manufactured from APP II with melamine modified according to own method.
TF-231 is different from TF-201 in the following properties:
-Obviously improve dispersibility and compatibility with polymers and resins;
-Increase fluidity of powder;
-Improve thermal expansion efficiency during inflaming retarding process and insulation performance.
Specification
|
Specification |
Value |
|
Appearance |
White powder |
|
P2O5 Content (w/w) |
≥64% |
|
N Content (w/w) |
≥17% |
|
Decomposition Temperature(TGA, Onset) |
≥265℃ |
|
Solubility (10% aqueous suspension, at 25ºC) |
≤0.7 |
|
Moisture (w/w) |
＜0.3% |
|
pH value (10% aqueous suspension, at 25ºC) |
7-9 |
|
Viscosity mPa.s (10% aqueous suspension, at 25 ºC) |
＜20 |
|
Average Particle size D50 |
15-25µm |
Product description:
Ammonium polyphosphate treated by melamine is a flame retardant based on phosphosrous / nitrogen synergism. free formaldehyde, manufactured from APP with melamine modified according to own method. it obviously imporve dispersibility and compatibility with polymers and resins as well as increase fluidity of powder . theremore it improve thermal expansion efficiency during inflaming retarding process and insulation performance
Applications:
1, used to prepare many kinds of high-efficiency intumescent coating
2, used as the main flameproof additive for expanding -type flame retardant used in plastic material of electron device , cable and rubber
3, Fiber materials (paper ,wood, fireproof textile)
4,Epxoy resin and unsaturated resin
Packing
25kg/bag, 24mt/20' fcl without pallets, 20mt/20'fcl with pallets.
Our service
1, Top standard and experience factory
2, High reliable for more than 10 years
3, standardized after sales service
Pre-sales service
* Prompt reply and professional team to provide good product
* Factory inspection support
* Sample is free for customer and will be retained for them
After -sales service
* Logistics information monitoring and following
* Documents service
for more information pls add Wechat: +0086 15928691963
Our Factory
Our Office
Our Lab
The exhibition
Recommended Products